I’m just a former Navy Nuke, but I see a major issue with this. Namely, by the time we retire ship-board nuclear reactors, they have been absorbing neutrons and radiation for 30 years, so the steel is weak enough that you could put a ball-peen hammer through it.
I’m just a former Navy Nuke, but I see a major issue with this. Namely, by the time we retire ship-board nuclear reactors, they have been absorbing neutrons and radiation for 30 years, so the steel is weak enough that you could put a ball-peen hammer through it.
The wiki on radiation embrittlement is pretty good reading for any mechanical engineers out there: https://en.wikipedia.org/wiki/Neutron_embrittlement